Abstract:
|
Polymer materials find application in optical storage technology,
namely in the development of high information density and fast access type
memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol
(PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized
and its comparison with methylene blue sensitized PVA in methanol and
complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented.
The optical absorption spectra of the thin films of these polymers
showed a strong and broad absorption region at 670-650 nm, matching the
wavelength of the laser used. A very slow recovery of the dye on irradiation was
observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8
and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction
efficiency of up to 20% was observed for the MBPVA/alcohol system and an
energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films
with a spatial frequency of 588 lines/mm. |