Now showing items 149-168 of 168
Abstract: | The growth of Fe–Ni based amorphous nanocolumns has been studied using atomic force microscopy. The root mean square roughness of the film surface increased with the deposition time but showed a little change at higher deposition time. It was found that the separation between the nanostructures increased sharply during the initial stages of growth and the change was less pronounced at higher deposition time. During the initial stages of the column growth, a roughening process due to self shadowing is dominant and, as the deposition time increases, a smoothening mechanism takes place due to the surface diffusion of adatoms |
Description: | APPLIED PHYSICS LETTERS 94, 063110 2009 |
URI: | http://dyuthi.cusat.ac.in/purl/4386 |
Files | Size |
---|---|
Surface evoluti ... lique angle deposition.pdf | (324.8Kb) |
Abstract: | Swift heavy ion induced changes in microstructure and surface morphology of vapor deposited Fe–Ni based metallic glass thin films have been investigated by using atomic force microscopy, X-ray diffraction and transmission electron microscopy. Ion beam irradiation was carried out at room temperature with 103 MeV Au9+ beam with fluences ranging from 3 1011 to 3 1013 ions/cm2. The atomic force microscopy images were subjected to power spectral density analysis and roughness analysis using an image analysis software. Clusters were found in the image of as-deposited samples, which indicates that the film growth is dominated by the island growth mode. As-deposited films were amorphous as evidenced from X-ray diffraction; however, high resolution transmission electron microscopy measurements revealed a short range atomic order in the samples with crystallites of size around 3 nm embedded in an amorphous matrix. X-ray diffraction pattern of the as-deposited films after irradiation does not show any appreciable changes, indicating that the passage of swift heavy ions stabilizes the short range atomic ordering, or even creates further amorphization. The crystallinity of the as-deposited Fe–Ni based films was improved by thermal annealing, and diffraction results indicated that ion beam irradiation on annealed samples results in grain fragmentation. On bombarding annealed films, the surface roughness of the films decreased initially, then, at higher fluences it increased. The observed change in surface morphology of the irradiated films is attributed to the interplay between ion induced sputtering, volume diffusion and surface diffusion |
Description: | Nuclear Instruments and Methods in Physics Research B 287 (2012) 85–90 |
URI: | http://dyuthi.cusat.ac.in/purl/4407 |
Files | Size |
---|---|
Swift heavy ion ... tion in metallic glass.pdf | (1.092Mb) |
Abstract: | Fe–Ni based amorphous thin films were prepared by thermal evaporation. These films were irradiated by 108 MeV Ag8+ ions at room temperature with fluences ranging from 1 1012 to 3 1013 ions/cm2 using a 15 UD Pelletron accelerator. Glancing angle x-ray diffraction studies showed that the irradiated films retain their amorphous nature. The topographical evolution of the films under swift heavy ion SHI bombardment was probed using atomic force microscope and it was noticed that surface roughening was taking place with ion beam irradiation. Magnetic measurements using a vibrating sample magnetometer showed that the coercivity of the films increases with an increase in the ion fluence. The observed coercivity changes are correlated with topographical evolution of the films under SHI irradiation. The ability to modify the magnetic properties via SHI irradiation could be utilized for applications in thin film magnetism |
Description: | J. Appl. Phys. 105, 033910 2009 |
URI: | http://dyuthi.cusat.ac.in/purl/4377 |
Files | Size |
---|---|
Swift heavy ion ... d amorphous thin films.pdf | (674.4Kb) |
Abstract: | Acicular FeC~O4-2H20 was precipitated from glycerol and starch media. Thermal decomposition of this oxalate in dry and moist nitrogen yielded primarily FeO and Fe 3Oa respectively. Characterization was attempted through DTA, TG, x-ray diffraction, TEM and magnetization studies. It was found that the oxalate can be completely decomposed to FeaO~ in moist nitrogen (PH~o ,"-" 35 torr) at 775 K and then oxidised by dry air to acicular "/-Fe~Oa at 575 K. The resulting material has saturation magnetization (,-,., 70 emu/g), coercive field (N300 Oe) and squareness ratio ( ,~, 0-60-0-65), which values art comparable with those of the commercial samples |
Description: | Bull. Mater. Sci,, Vol, 3, Number 3, November 1981, pp. 275-280. |
URI: | http://dyuthi.cusat.ac.in/purl/4419 |
Files | Size |
---|---|
Synthesis and c ... magnetic tape material.pdf | (317.5Kb) |
Abstract: | Bio-compatible magnetic fluids having high saturation magnetization find immense applications in various biomedical fields. Aqueous ferrofluids of superparamagnetic iron oxide nanoparticles with narrow size distribution, high shelf life and good stability is realized by controlled chemical co-precipitation process. The crystal structure is verified by X-ray diffraction technique. Particle sizes are evaluated by employing Transmission electron microscopy. Room temperature and low-temperature magnetic measurements were carried out with Superconducting Quantum Interference Device. The fluid exhibits good magnetic response even at very high dilution (6.28 mg/cc). This is an advantage for biomedical applications, since only a small amount of iron is to be metabolised by body organs. Magnetic field induced transmission measurements carried out at photon energy of diode laser (670 nm) exhibited excellent linear dichroism. Based on the structural and magnetic measurements, the power loss for the magnetic nanoparticles under study is evaluated over a range of radiofrequencies. |
URI: | http://dyuthi.cusat.ac.in/purl/2964 |
Files | Size |
---|---|
Dyuthi-P00409.pdf | (443.7Kb) |
Abstract: | Magnetic heterostructures with carbon nanotubes having multiple functionalities are fascinating materials which can be manipulated by means of an external magnetic field. In this paper we report our investigations on the synthesis and optical limiting properties of pristine cobalt nanotubes and high coercivity cobalt-in-carbon nanotubes (a new nanosystem where carbon nanotubes are filled with cobalt nanotubes). A general mobility assisted growth mechanism for the formation of one-dimensional nanostructures inside nanopores is verified in the case of carbon nanotubes. The open-aperture z-scan technique is employed for the optical limiting measurements in which nanosecond laser pulses at 532 nm have been used for optical excitation. Compared to the benchmark pristine carbon nanotubes these materials show an enhanced nonlinear optical absorption, and the nonlinear optical parameters calculated from the data show that these materials are efficient optical limiters. To the best of our knowledge this is the first report where the optical limiting properties of metal nanotubes are compared to those of carbon nanotubes |
Description: | Nanotechnology 20 (2009) 285702 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4370 |
Files | Size |
---|---|
The synthesis o ... cal limitingproperties.pdf | (1.704Mb) |
Abstract: | Cobalt nanotubes (CoNTs) with very high longitudinal coercivity were prepared by electrodeposition of cobalt acetate for the first time by using anodized alumina (AAO) template. They were then characterized with X-ray diffraction (XRD), a field emission scanning electron microscope (FESEM), and a transmission electron microscope (TEM). Formation of a highly ordered hexagonal cobalt phase is observed. Room temperature SQUID (superconducting quantum interference device) magnetometer measurements indicate that the easy axis of magnetization is parallel to the nanotube axis. These CoNTs exhibit very high longitudinal coercivity of ∼820 Oe. A very high intertubular interaction resulting from magnetostatic dipolar interaction between nanotubes is observed. Thick-walled nanotubes were also fabricated by using cobalt acetate tetrahydrate precursors. A plausible mechanism for the formation of CoNTs based on mobility assisted growth is proposed. The role of the hydration layer and the mobility of metal ions are elucidated in the case of the growth mechanism of one-dimensional geometry |
Description: | J. Phys. Chem. C 2008, 112, 14281–14285 |
URI: | http://dyuthi.cusat.ac.in/purl/4362 |
Files | Size |
---|---|
Synthesis of Hi ... he Mechanism of Growth.pdf | (1.794Mb) |
Abstract: | Hybrid magnetic nanostructures with high coercivity have immense application potential in various fields. Nickel (Ni) electrodeposited inside Cobalt (Co) nanotubes (a new system named Ni @ Co nanorods) were fabricated using a two-step potentiostatic electrodeposition method. Ni @ Co nanorods were crystalline, and they have an average diameter of 150 nm and length of *15 lm. The X-ray diffraction studies revealed the existence of two separate phases corresponding to Ni and Co. Ni @ Co nanorods exhibited a very high longitudinal coercivity. The general mobility-assisted growth mechanism proposed for the growth of one-dimensional nanostructures inside nano porous alumina during potentiostatic electrodeposition is found to be valid in this case too |
Description: | Nanoscale Res Lett (2010) 5:164–168 |
URI: | http://dyuthi.cusat.ac.in/purl/4375 |
Files | Size |
---|---|
Synthesis of Hi ... ir Magnetic Properties.pdf | (349.6Kb) |
Abstract: | Nanocomposites based on natural rubber and nano-sized nickelwere synthesized by incorporating nickel nanoparticles in a natural rubber matrix for various loadings of the filler. Structural, morphological, magnetic and mechanical properties of the compositeswere evaluated along with a detailed study of dielectric properties. Itwas found that nickel particleswere uniformly distributed in the matrix without agglomeration resulting in a magnetic nanocomposite. The elastic properties showed an improvement with increase in filler content but breaking stress and breaking strain were found to decrease. Dielectric permittivity was found to decrease with increase in frequency, and found to increase with increase in nickel loading. The decrease in permittivity with temperature is attributed to the high volume expansivity of rubber at elevated temperatures. Dielectric loss of blank rubber as well as the composites was found to increase with temperature. |
URI: | http://dyuthi.cusat.ac.in/purl/2834 |
Files | Size |
---|---|
Dyuthi-P00390.pdf | (1.102Mb) |
Abstract: | Stable, OH free zinc oxide (ZnO) nanoparticles were synthesized by hydrothermal method by varying the growth temperature and concentration of the precursors. The formation of ZnO nanoparticles were confirmed by x-ray diffraction (XRD), transmission electron microscopy (TEM) and selected area electron diffraction (SAED) studies. The average particle size have been found to be about 7-24 nm and the compositional analysis is done with inductively coupled plasma atomic emission spectroscopy (ICP-AES). Diffuse reflectance spectroscopy (DRS) results shows that the band gap of ZnO nanoparticles is blue shifted with decrease in particle size. Photoluminescence properties of ZnO nanoparticles at room temperature were studied and the green photoluminescent emission from ZnO nanoparticles can originate from the oxygen vacancy or ZnO interstitial related defects. |
URI: | http://dyuthi.cusat.ac.in/purl/790 |
Files | Size |
---|---|
Synthesis of Zn ... by hydrothermal method.pdf | (1.906Mb) |
Abstract: | Rubber ferrite composites containing various mixed ferrites were prepared for different compositions and various loadings. The magnetic and dielectric properties of the fillers as well as the ferrite filled matrixes were evaluated separately. The results are correlated. Simple equations are proposed to predetermine the magnetic and dielectric properties. The validity of these equations is verified and they are found to be in good agreement. These equations are useful in tailoring the magnetic and dielectric properties of these composites with predetermined properties |
Description: | Bull. Mater. Sci., Vol. 24, No. 6, December 2001, pp. 623–631 |
URI: | http://dyuthi.cusat.ac.in/purl/4361 |
Files | Size |
---|---|
Tailoring magne ... taining mixed ferrites.pdf | (198.4Kb) |
Abstract: | Polarized Raman spectral changes with respect to temperature were investigated for Pr(BrO3)3·9H2O single crystals. FTIR spectra of hydrated and deuterated analogues were also recorded and analysed. Temperature dependent Raman spectral variation have been explained with the help of the thermograms recorded for the crystal. Factor group analysis could propose the appearance ofBrO3 ions at sites corresponding to C3v (4) and D3h (2). Analysis of the vibrational bands at room temperature confirms a distorted C3v symmetry for the BrO3 ion in the crystal. From the vibrations of water molecules, hydrogen bonds of varying strengths have also been identified in the crystal. The appearance υ1 mode of BrO3− anion at lower wavenumber region is attributed to the attachment of hydrogen atoms to the BrO3− anion. At high temperatures, structural rearrangement is taking place for bothH2Omolecule and BrO3 ions leading to the loss ofwater molecules and structural reorientation of bromate ions causing phase transition of the crystal at the temperature of 447 K. |
Description: | Spectrochimica Acta Part A 64 (2006) 518–525 |
URI: | http://dyuthi.cusat.ac.in/purl/4557 |
Files | Size |
---|---|
Temperature dep ... id (Pr) single crystal.pdf | (184.5Kb) |
Abstract: | Potential applications of nickel nanoparticles demand the synthesis of self-protected nickel nanoparticles by different synthesis techniques. A novel and simple technique for the synthesis of self-protected nickel nanoparticles is realized by the inter-matrix synthesis of nickel nanoparticles by cation exchange reduction in two types of resins. Two different polymer templates namely strongly acidic cation exchange resins and weakly acidic cation exchange resins provided with cation exchange sites which can anchor metal cations by the ion exchange process are used. The nickel ions which are held at the cation exchange sites by ion fixation can be subsequently reduced to metal nanoparticles by using sodium borohydride as the reducing agent. The composites are cycled repeating the loading reduction cycle involved in the synthesis procedure. X-Ray Diffraction, Scanning Electron Microscopy, Transmission Electron microscopy, Energy Dispersive Spectrum, and Inductively Coupled Plasma Analysis are effectively utilized to investigate the different structural characteristics of the nanocomposites. The hysteresis loop parameters namely saturation magnetization and coercivity are measured using Vibrating Sample Magnetometer. The thermomagnetization study is also conducted to evaluate the Curie temperature values of the composites. The effect of cycling on the structural and magnetic characteristics of the two composites are dealt in detail. A comparison between the different characteristics of the two nanocomposites is also provided |
Description: | Nanoscale Res Lett (2010) 5:889–897 |
URI: | http://dyuthi.cusat.ac.in/purl/4390 |
Files | Size |
---|---|
Template-Assist ... edNickel Nanoparticles.pdf | (815.2Kb) |
Abstract: | Thermal diffusivity of the composites of camphor sulphonic acid (CSA) doped polyaniline (PANI) and its composites with cobalt phthalocyanine (CoPc) has been measured using open cell photoacoustic technique. Analysis of the data shows that the effective thermal diffusivity value can be tuned by varying the relative volume fraction of the constituents. It is seen that polaron assisted heat transfer mechanism is dominant in CSA doped PANI and these composites exhibit a thermal diffusivity value which is intermediate to that of CSA doped PANI and CoPc. The results obtained are correlated with the electrical conductivity and hardness measurements carried out on the samples |
URI: | http://dyuthi.cusat.ac.in/purl/1827 |
Files | Size |
---|---|
Dyuthi-P00385.pdf | (45.66Kb) |
Abstract: | Transparent diode heterojunction on ITO coated glass substrates was fabricated using p-type AgCoO2 and n-type ZnO films by pulsed laser deposition (PLD). The PLD of AgCoO2 thin films was carried out using the pelletized sintered target of AgCoO2 powder, which was synthesized in-house by the hydrothermal process. The band gap of these thin films was found to be ~3.89 eV and they had transmission of~55% in the visible spectral region. Although Hall measurements could only indicate mixed carrier type conduction but thermoelectric power measurements of Seebeck coefficient confirmed the p-type conductivity of the grown AgCoO2 films. The PLD grown ZnO films showed a band gap of ~3.28 eV, an average optical transmission of ~85% and n-type carrier density of~4.6×1019 cm− 3. The junction between p-AgCoO2 and n-ZnO was found to be rectifying. The ratio of forward current to the reverse current was about 7 at 1.5 V. The diode ideality factor was much greater than 2. |
URI: | http://dyuthi.cusat.ac.in/purl/791 |
Files | Size |
---|---|
Synthesis of Zn ... by hydrothermal method.pdf | (1.906Mb) |
Abstract: | The red cells found in the red rain in Kerala, India are now considered as a possible case of extraterrestrial life form. These cells can undergo rapid replication even at an extreme high temperature of 300 deg C. They can also be cultured in diverse unconventional chemical substrates. The molecular composition of these cells is yet to be identified. This paper reports the unusual autofluorescence characteristic of the cultured red rain cells. A spectrofluorimetric study has been performed to investigate this, which shows a systematic shift of the fluorescence emission peak wavelength as the excitation wavelength is increased. Conventional biomolecules are not known to have this property. Details of this investigation and the results are discussed. |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1973 |
Files | Size |
---|---|
Godfry, Louis.pdf | (553.2Kb) |
Abstract: | Roughness and defects induced on few-layer graphene (FLG) irradiated by Ar+ ions at different energies were investigated using X-ray photoemission spectroscopy (XPS) and atomic force microscopy techniques. The results provide direct experimental evidence of ripple formation, sp2 to sp3 hybridized carbon transformation, electronic damage, Ar+ implantation, unusual defects and edge reconstructions in FLG, which depend on the irradiation energy. In addition, shadowing effects similar to those found in oblique-angle growth of thin films were seen. Reliable quantification of the transition from the sp2-bonding to sp3-hybridized state as a result of Ar+ ion irradiation is achieved from the deconvolution of the XPS C (1s) peak. Although the ion irradiation effect is demonstrated through the shape of the derivative of the Auger transition C KVV spectra, we show that the D parameter values obtained from these spectra which are normally used in the literature fail to account for the sp2 to sp3 hybridization transition. In contrast to what is known, it is revealed that using ion irradiation at large FLG sample tilt angles can lead to edge reconstructions. Furthermore, FLG irradiation by low energy of 0.25 keV can be a plausible way of peeling graphene layers without the need of Joule heating reported previously |
Description: | Al-Harthi et al. Nanoscale Research Letters 2012, 7:466 |
URI: | http://dyuthi.cusat.ac.in/purl/4412 |
Files | Size |
---|---|
Unusual surface ... ayer graphene surfaces.pdf | (838.7Kb) |
Abstract: | FTIR and Raman spectra of FeClMoO4 single crystal and polycrystalline Na2MoO4, Na2MoO4·2H2O and Na2MoO4·2D2O are recorded and analysed. The band positions for different modes suggest that MoO4 tetrahedron is more distorted in FeClMoO4. The larger splitting observed for the bending modes and partial retention of degeneracy of the asymmetric stretching mode indicate that angular distortion is greater than liner distortion in MoO4 2 ion in FeClMoO4 confirming x-ray data. The non-appearance of the n1 and n2 modes in the IR and partial retention of the degeneracies of various modes show that MoO4 2 ion retains Td symmetry in Na2MoO4. Wavenumber values of the n1 mode indicate that the distortion of MoO4 tetrahedra in the four crystals are in the order FeClMoO4\ Na2MoO4·2H2O\Na2MoO4·2D2O\Na2MoO4. The water bands suggest the presence of two crystallographically distinct water molecules in Na2MoO4·2H2O. They form strong hydrogen bonds |
Description: | Spectrochimica Acta Part A 53 (1997) 867–876 |
URI: | http://dyuthi.cusat.ac.in/purl/4564 |
Files | Size |
---|---|
Vibrational spe ... oO4 andNa2MoO4·2H2OD2O.pdf | (415.4Kb) |
Abstract: | The Raman and FTIR spectra of [C(NH2)3]2M(SO4)2 ·6H2O (withM= Co, Fe, Ni) were recorded and analysed. The observed spectral bands are assigned in terms of vibrations of guanidinium ions, sulphate groups and water molecules. The analysis shows that the sulphate tetrahedra are distorted from their free state symmetry Td to C1. This is attributed to the presence of hydrogen bonds from water molecules. The order of distortion of the metal oxygen octahedra influenced the distortion of the sulphate tetrahedra. The appearance of 1– 3 modes of water molecules above 3300 cm−1 indicates the presence of weak hydrogen bonds |
Description: | Solid State Communications 143 (2007) 348–352 |
URI: | http://dyuthi.cusat.ac.in/purl/4551 |
Files | Size |
---|---|
Vibrational spe ... sulphatehexahydrates [MII | (395.3Kb) |
Abstract: | Th(BrO3)3·H2O single crystals were grown from its aqueous solution at room temperature. Single crystal XRD, Raman and FTIR techniques were used to investigate the crystal structure. The crystal structure was solved by Patterson method. The as grown crystals are in monoclinic system with space group P21/c. The unit cell parameters are a = 12.8555(18) Å, b = 7.8970(11) Å, c = 9.0716(10) Å, = 90°, = 131.568° and = 90° and unit cell volume is 689.1(2) Å3. Z = 8, R factor is 5.9. The Raman and FTIR studies indicate the lowering of symmetry of bromate anion from C3V to C1. Hydrogen bonds with varying strengths are present in the crystal. The centrosymmetric space group P21/c of the crystal is confirmed by the non-coincidence of majority of Raman and IR bands |
Description: | Crystal Structure Theory and Applications, 2013, 2, 70-74 |
URI: | http://dyuthi.cusat.ac.in/purl/4561 |
Files | Size |
---|---|
X-Ray Crysatllo ... horium Bromate Hydrate.pdf | (592.1Kb) |
Now showing items 149-168 of 168
Dyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.