Sankara Raman, S; Nampoori, V P N; Vallabhan, C P G; Ambadas, G; Sugunan, S(American Institute of Physics, February 1, 1999)
[+]
[-]
Abstract:
The effect of the chemisorbed hydroxyl groups on the thermal diffusivity of gama alumina is determined
by evaluating the thermal diffusivity at various degassing temperatures and by doping it with rare
earth oxide using photoacoustic technique. The thermal diffusivity is found to decrease with the
increase in degassing temperature as well as with the increase in the doping concentration of rare
earth oxide. This decrease has been attributed to the loss of hydroxyl ion from the y-Al2O3.
V P N Nampoori; Radhakrishnan, P; Girijavallabhan, C P; Sajan, D George(Physical Review, American Physical Society, 2003)
[+]
[-]
Abstract:
In this paper, we report the in-plane and cross-plane measurements of the thermal diffusivity of double
epitaxial layers of n-type GaAs doped with various concentrations of Si and a p-type Be-doped GaAs layer
grown on a GaAs substrate by the molecular beam epitaxial method, using the laser-induced nondestructive
photothermal deflection technique. The thermal diffusivity value is evaluated from the slope of the graph of the
phase of the photothermal deflection signal as a function of pump-probe offset. Analysis of the data shows that
the cross-plane thermal diffusivity is less than that of the in-plane thermal diffusivity. It is also seen that the
doping concentration has a great influence on the thermal diffusivity value. Measurement of p-type Be-doped
samples shows that the nature of the dopant also influences the effective thermal diffusivity value. The results
are interpreted in terms of a phonon-assisted heat transfer mechanism and the various scattering process
involved in the propagation of phonons
Joseph, L K; Sanjay, G; Suja, H; Sugunan, S; Nampoori, V P N; Radhakrishnan, P(Taylor & Francis, April 1, 2009)
[+]
[-]
Abstract:
Thermal diffusivity (TD) measurements were performed on some industrially
important dyes – auramine O (AO), malachite green and methylene blue (MB) –
adsorbed K-10 montmorillonites using photoacoustic method. The TD value for
the dye-adsorbed clay mineral was observed to change with a variation in dye
concentration. The contribution of the dye towards TD was also determined. The
repeatedly adsorbed samples with MB and AO exhibited a lower TD than the
single-adsorbed samples. TD values of sintered MB samples were also obtained
experimentally. These sintered samples exhibit a higher TD, although they show
a trend similar to that of non-sintered pellets. A variation in dye concentration
and sintering temperature can be used for tuning the TD value of the clay mineral
to the desired level.
Nampoori, V P N; Radhakrishnan, P; Girijavallabhan, C P; Sajan, D George(Journal of Physics D : Applied Physics, Institute of Physics Publishing, April 2, 2003)
[+]
[-]
Abstract:
An open photoacoustic cell operating in the low range of chopping
frequency has been employed to evaluate the thermal diffusivity values of
intrinsic InP and InP doped with S, Sn and Fe. The experimental set-up is
calibrated by the evaluation of thermal diffusivity value of pure Si and
GaAs. The present investigation shows that doped samples show a reduced
value for thermal diffusivity compared to intrinsic sample. From the
analysis of data it is also seen that nature of dopant clearly influences the
thermal diffusivity value of semiconductors. The results are explained in
terms of phonon assisted heat transfer mechanism in semiconductors