Now showing items 1-8 of 8
Abstract: | A new microwave dielectric resonator Ba(Tb1/2Nb1/2)03 has been prepared and characterized in the microwave frequency region. 1 wt% CeO2 is used as additive to reduce the sintering temperature. The sintered samples were characterized by XRD, SEM and Raman spectroscopic methods. Microwave DR properties such as er, Q factor and temperature-coefficient of resonant frequency (Ti) have been measured using a HP 8510 B Network Analyzer. Cylindrical DRs of Ba(Tb1/2Nbi/2)03 showed high Er (~ 37), high Q (~3,200) and low Tf (~10 ppm /°C) at 4 GHz and hence are useful for practical applications |
URI: | http://dyuthi.cusat.ac.in/purl/1447 |
Files | Size |
---|---|
Ba(Tb1 2Nb1 2)0 ... e dielectric resonator.PDF | (2.173Mb) |
Abstract: | Infrared and polarized Raman spectra of Cu(HSeO3) 2 - H20 single crystal have been recorded and analysed. The appearance of non-degenerate Se-OH stretching vibrations in the ~x: and ~y: polarizations of Raman spectra indicate distortion of the HSeO~- ion in the Cu(HSeO3)2 - H20 crystal. The low wavenumber values obtained for the symmetric and asymmetric stretching vibrations of the HSeO 3 ion are consistent with the strong hydrogen bonding and the influence of Jahn-Teller distortion as predicted in X-ray diffraction data. The shifting of the stretching and bending vibrations of the hydroxyl groups and water molecules from the free state values also confirms the strong hydrogen bonding in this crystal. Broad bands observed for both stretching and bending regions become sharp in the Raman spectrum recorded at 77 K. A doublet appears for the Se-OH stretching mode at this temperature indicating the settling of protons in an ordered position and the absence of intrabond proton tunnelling |
Description: | Speetrochimica Acta Part A 51 (1995) 1509-1515 |
URI: | http://dyuthi.cusat.ac.in/purl/4553 |
Files | Size |
---|---|
Infrared and po ... 2 • H20 single crystal.pdf | (370.5Kb) |
Abstract: | A microwave dielectric ceramic resonator based on BaCe2Ti5O15 and Ba5Nb4O15 have been prepared by conventional solid state ceramic route. The dielectric resonators (DRs) have high dielectric constant 32 and 40 for BaCe2Ti5O15 and Ba5Nb4O15, respectively. The whispering gallery mode (WGM) technique was employed for the accurate determination of the dielectric properties in the microwave frequency range. The BaCe2Ti5O15 and Ba5Nb4O15 have quality factors (Q X F) of 30,600 and 53,000 respectively. The quality factor is found to depend on the azimuthal mode numbers. The temperature coefficient of resonant frequency (Tr) of BaCe2Ti5O15 and Ba5Nb4O15 have been measured accurately using different resonant modes and are + 41 and + 78 ppm/K, respectively |
URI: | http://dyuthi.cusat.ac.in/purl/1446 |
Files | Size |
---|---|
Microwave chara ... ng gallery mode method.PDF | (2.989Mb) |
Abstract: | The BaO-2CeO2-nTiO2 ceramics with n = 3, 4 and 5 have been prepared with CeO2 as starting material . The ceramics have been characterized using scanning electron microscopy , X-ray diffraction , Raman and X-ray photoelectron spectroscopy techniques. The microwave dielectric properties have been measured using standard dielectric resonator techniques . BaO-2CeO2-3TiO2 (123), BaO-2CeO2-4TiO2 ( 124) and BaO-2CeO2-5TiO2 ( 125) ceramics showed dielectric constants of 38, 27 and 32, respectively . All the ceramics showed fairly good unloaded Q - factors . 124 and 125 compounds exhibited low tf values, while 123 showed a high rf value |
URI: | http://dyuthi.cusat.ac.in/purl/1493 |
Files | Size |
---|---|
Microwave diele ... -2CeO2-nTiO2 ceramics.PDF | (3.306Mb) |
Abstract: | New dielectric ceramics with formula BaTi3Nb4, O„ and Ba6Til4Nbz039 have been prepared and characterized. BaTi3Nba017 was densified to 92% of TD after firing at 1310 oC for 4 h. However, Ba6Ti 1 4Nb2O39 fired under optimized conditions (1260 ` C for 4 h) showed only 85% TD together with secondary phase. The crystal system of both of the compositions is orthorhombic |
URI: | http://dyuthi.cusat.ac.in/purl/1443 |
Files | Size |
---|---|
New high permit ... TiO2-Nb2O5 composition.PDF | (2.094Mb) |
Abstract: | The dielectric ceramics BaNd2Ti3Oto, BaNd2Ti4O12 and BaNd2Ti5O14 have been prepared by Conventional solid state ceramic route. The sintered ceramic samples have been characterized by X-ray diffraction and Scanning Electron Microscopy (SEM). The dielectric properties in the microwave frequency range have been measured using conventional microwave dielectric resonator methods. The BaNd2Ti1O10, BaN2Ti4O12 and BaNd2Ti5O14 have dielectric constants (Er) ~ 60, 84 and 77 respectively. They have relatively high quality factors |
URI: | http://dyuthi.cusat.ac.in/purl/1444 |
Files | Size |
---|---|
Preparation,cha ... BaO-Nd2O3-TiO2 system.PDF | (2.220Mb) |
Abstract: | Microwave dielectric resonators (DRs) based on Ba(B1,2Nbi/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb, and In] complex perovskites have been prepared by conventional solid state ceramic route. The dielectric properties (relative permittivity, Er; quality factor, Q; and resonant frequency, rr) of the ceramics have been measured in the frequency range 4-6 GHz using resonance methods. The resonators have relatively high dielectric constant in the range 36-45, high quality factor and small temperature variation of resonant frequency. The dielectric properties are found to depend on the tolerance factor (t), ionic radius (r), and lattice parameter (ap) |
URI: | http://dyuthi.cusat.ac.in/purl/1494 |
Files | Size |
---|---|
Preparation, ch ... Y, Yb and In] ceramics.PDF | (4.468Mb) |
Abstract: | Raman spectra of the KTP single crystal are recorded in electric fields (dc and ac) applied along the polar axis c. Spectra with the laser beam focused near the cathode end, anode end and the centre of the crystal are recorded. The cathode end of the crystal develops a spot ‘grey track’ where the laser beam is focused after a lapse of 5 h from the application of a dc electric field of 38 V/cm. The spectra recorded at the cathode end after the application of field show variations in intensity of bands. A new band appears at 177 cm21. Changes in band intensities are explained on the basis of changes in polarizability of the crystal due to the movement of K1 ions along the polar axis. K1 ions accumulate at the cathode end, where the ‘Grey track’ formation occurs. The intensity enhancement observed for almost all bands in the ac field is attributed to the improvement of crystalline quality. |
Description: | Journal of Physics and Chemistry of Solids 60 (1999) 1983–1988 |
URI: | http://dyuthi.cusat.ac.in/purl/4548 |
Files | Size |
---|---|
Raman spectra o ... in situ electric field.pdf | (348.1Kb) |