| Abstract: | Zinc salts of ethyl, isopropyl and butyl xanthates were prepared in the laboratory. The effect of these xanthates with zinc diethyldithiocarbamate (ZDC) on the vulcanization of HAF filled NR compound has been studied at different temperatures. The rubber compounds with the three xanthate accelerators and ZDC were cured at various temperatures from 60°C to 150°C. The sheets were moulded and properties such as tensile strength , tear strength , cross-link density, elongation -at-break, compression set, heat build up, abrasion resistance, flex resistance , etc. were evaluated . The properties showed that zinc xanthate/ZDC accelerator combination has a positive synergistic effect on the mechanical properties of NR compounds. The curing of HAF filled NR compound containing zinc xanthate /ZDC is slightly slower than the curing of the corresponding gum compounds . It is observed that, by gradually increasing the amount of the accelerator, the cure time of black filled NR compound can be made equal to that of the gum compou |
| URI: | http://dyuthi.cusat.ac.in/purl/814 |
| Files | Size |
|---|---|
| Shiny Palaty an ... nergism of...,July2003.PDF | (5.107Mb) |
| Abstract: | The thesis entitled “Synergistic solvent extraction of Thorium(IV) and Uranium(VI) with β-diketones in presence of oxo-donors” embodies the results of the investigations carried out on the extraction of thorium(IV) an uranium(VI) with heterocyclic β-diketones in the presence and absence of various macrocyclic ligands and neutral organophosphorus extractants. The objective of this work is to generate the knowledge base to achieve better selectivity between thorium(IV) and uranium(VI) by understanding the interactions of crown ethers or neutral organophosphorus extractants with metal-heterocyclic β-diketonate complexes. Para-substituted 1-phenyl-3-methyl-4-aroyl-5-pyrazolones, namely,1-phenyl-3-methyl-4-(4-fluorobenzoyl)-5-pyrazolone (HPMFBP) and 1-phenyl-3-methyl-4-(4-toluoyl)-5-pyrazolone (HPMTP) were synthesized and characterized by elemental analysis, IR and H NMR spectral data. The synthesized ligands have been utilized for the extraction of thorium(IV) and uranium(VI) from nitric acid solutions in the presence and absence of various crown ethers. Thorium(IV) and uranium(VI) complexes with HPMPP(1-Phenyl-3-methyl-4-pivaloyl-5-pyrazolone) and neutral organophosphorus extractants were synthesized and characterized by IR and P NMR spectral data to further understand the interactions of neutral organophosphorus extractants with metal-chelates. Solid complexes of thorium(IV) and uranium(VI) with para-substituted 4-aroyl-5-isoxazolones and crown ethers were isolated and characterized by various spectroscopic techniques to further clarify the nature of the extracted complexes. |
| URI: | http://dyuthi.cusat.ac.in/purl/912 |
| Files | Size |
|---|---|
| Dyuthi-T0294.pdf | (2.603Mb) |
| Abstract: | Due to the emergence of multiple language support on the Internet, machine translation (MT) technologies are indispensable to the communication between speakers using different languages. Recent research works have started to explore tree-based machine translation systems with syntactical and morphological information. This work aims the development of Syntactic Based Machine Translation from English to Malayalam by adding different case information during translation. The system identifies general rules for various sentence patterns in English. These rules are generated using the Parts Of Speech (POS) tag information of the texts. Word Reordering based on the Syntax Tree is used to improve the translation quality of the system. The system used Bilingual English –Malayalam dictionary for translation. |
| Description: | 2012 International Conference on Data Science & Engineering (ICDSE) |
| URI: | http://dyuthi.cusat.ac.in/purl/4108 |
| Files | Size |
|---|---|
| Syntactic Based ... m English to Malayalam.pdf | (134.8Kb) |
| Abstract: | Four manganese(II) complexes Mn2(paa)2(N3)4 (1), [Mn(paa)2(NCS)2] 3/2H2O (2), Mn(papea)2(NCS)2 (3), [Mn(dpka)2(NCS)2] 1/2H2O(4) of three neutral N,N donor bidentate Schiff bases were synthesized and physico- chemically characterized by means of partial elemental analyses, electronic, infrared and EPR spectral studies. Compounds 3 and 4 were obtained as single crystals suitable for X-ray diffraction. Compound 4 recrystallized as Mn(dpka)2(NCS)2. Both the compounds crystallized in the monoclinic space groups P21 for 3 and C2/c for 4. Manganese(II) is found to be in a distorted octahedral geometry in both the monomeric complexes with thiocyanate anion as a terminal ligand coordinating through the nitrogen atom. EPR spectra in DMF solutions at 77 K show hyperfine sextets with low intensity forbidden lines lying between each of the two main hyperfine lines and the zero field splitting parameters (D and E) were calculated. |
| Description: | Polyhedron 29 (2010) 2643–2650 |
| URI: | http://dyuthi.cusat.ac.in/purl/4707 |
| Files | Size |
|---|---|
| Syntheses, EPR ... s and azidethiocyanate.pdf | (1.153Mb) |
| URI: | http://dyuthi.cusat.ac.in/purl/1742 |
| Files | Size |
|---|---|
| Dyuthi-T0301.pdf | (3.647Mb) |
| Abstract: | The thesis deals with studies on the synthesis, characterisation and catalytic applications of some new transition metal complexes of the Schiff bases derived from 3-hydroxyquinoxaline 2-carboxaldehyde.. Schiff bases which are considered as ‘privileged ligands’ have the ability to stabilize different metals in different oxidation states and thus regulate the performance of metals in a large variety of catalytic transformations. The catalytic activity of the Schiff base complexes is highly dependant on the environment about the metal center and their conformational flexibility. Therefore it is to be expected that the introduction of bulky substituents near the coordination sites might lead to low symmetry complexes with enhanced catalytic properties. With this view new transition metal complexes of Schiff bases derived from 3-hydroxyquinoxaline-2-carboxaldehyde have been synthesised. These Schiff bases have more basic donor nitrogen atoms and the presence of the quinoxaline ring may be presumed to build a favourable topography and electronic environment in the immediate coordination sphere of the metal. The aldehyde was condensed with amines 1,8-diaminonaphthalene, 2,3-diaminomaleonitrile, 1,2-diaminocyclohexane, 2-aminophenol and 4-aminoantipyrine to give the respective Schiff bases. The oxovanadium(IV), copper(II) and ruthenium(II)complexes of these Schiff bases were synthesised and characterised. All the oxovanadium(IV) complexes have binuclear structure with a square pyramidal geometry. Ruthenium and copper form mononuclear complexes with the Schiff base derived from 4- aminoantipyrine while binuclear square planar complexes are formed with the other Schiff bases. The catalytic activity of the copper complexes was evaluated in the hydroxylation of phenol with hydrogen peroxide as oxidant. Catechol and hydroquinone are the major products. Catalytic properties of the oxovanadium(IV) complexes were evaluated in the oxidation of cyclohexene with hydrogen peroxide as the oxidant. Here allylic oxidation products rather than epoxides are formed as the major products. The ruthenium(II) complexes are found to be effective catalysts for the hydrogenation of benzene and toluene. The kinetics of hydrogenation was studied and a suitable mechanism has been proposed. |
| Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1930 |
| Files | Size |
|---|---|
| Dyuthi-T0483.pdf | (11.90Mb) |
| Abstract: | Chemically modified novel thermo-reversible zinc sulphonated ionomers based on natural rubber (NR), radiation induced styrene grafted natural rubber (RI-SGNR), and chemically induced styrene grafted natural rubber (CI-SGNR) were synthesized using acetyl sulphate/zinc acetate reagent system. Evidence for the attachment of sulphonate groups has been furnished by FTIR spectra. which was supplanted by FTNMR results. Estimation of the zinc sulphonate group was done using spectroscopic techniques such as XRFS and ICPAES. The TGA results prove improvement in the therrno-oxidative stability of the modified natural rubber. Both DSC and DMTA studies show that the incorporation of the ionic groups affect the thermal transition of the base polymer. Retention of the improved physical properties of the novel ionomers even after three repeated cycles of mastication and molding at 120 degree C may be considered as the evidence for the reprocessabiJity of the ionomer. Effect of both particulate (carbon black. silica & zinc stearate) and fibrous fillers (nylon & glass) on the properties of the radiation induced styrene grafted natural rubber ionomer has been evaluated. Incorporation of HAF carbon black results in maximum improvement in physical properties. Silica reinforces the backbone chain and weakens the ionic associations. Zinc stearate plays the dual role of reinforcement and ptasticization. The nylon and glass filled lonorner compounds show good improvement in the physical properties in comparison with the neat ionomer. Dispersion and adhesion of the fillers in the ionomer matrix has been amply supported by their SEM micrographs. Microwave probing of the electrical behavior of the 26.5 ZnSRISGNR ionomer reveals that the maximum relative complex conductivity and the complex permittivity appear at the frequency of 2.6 GHz. The complex conductivity of the base polymer increases from 1.8x 10.12 S/cm to 3.3xlO·4 S/cm. Influence of fillers on the dielectric constant and conductivity of the new ionic thermoplastic elastomer has been studied. The ionomer I nylon compound shows the highest microwave conductivity. Use of the 26.5 ZnS-RISGNR ionomer as a compatibilizer for obtaining the technologically compatible blends from the immiscible SBR/NBR system has been verified. The heat fugitive ionic cross-linked natural rubber may be, therefore, useful as an alternative to vulcanized rubber and thermoplastic elastomer |
| Description: | Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/2187 |
| Files | Size |
|---|---|
| Dyuthi-T0538.pdf | (6.118Mb) |
| Description: | Department of Physics, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/2517 |
| Files | Size |
|---|---|
| Dyuthi-T0676.pdf | (7.299Mb) |
| Abstract: | The objective of the present study is the formation of single phase Zn1−xTMxO thin films by PLD and increase the solubility limit of TM dopants. The TM doped ZnO nanostructures were also grown by hydrothermal method. The structural and morphological variation of ZnO:TM thin films and nanostructures with TM doping concentration is also investigated. The origin and enhancement of ferromagnetism in single phase Zn1−xTMxO thin films and nanostructures using spectroscopic techniques were also studied. The dependence of ablation parameters on the structural and optical properties of ZnO thin films were studied |
| Description: | Department of Physics Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/4628 |
| Files | Size |
|---|---|
| Dyuthi-T1820.pdf | (16.84Mb) |
| Abstract: | ABSTRACT: p-Phenylenediamine was chemically attached to low molecular weight chlorinated paraffin wax. The polymer-bound p-phenylenediamine was characterized by vapor-phase osmometry (VPO), proton magnetic resonance spectroscopy ('H-NMR), infrared spectroscopy (IR), and thermogravimetric analysis (TGA). The efficiency and permanence of the polymer-bound p-phenylenediamine as an antioxidant was compared with a conventional amine-type antioxidant in natural rubber vulcanizates. The vulcanizates showed improved aging resistance in comparison to vulcanizates containing a conventional antioxidant. The presence of liquid polymer-bound p-phenylenediamine also reduces the amount of the plasticizer required for compounding. |
| URI: | http://dyuthi.cusat.ac.in/purl/861 |
| Files | Size |
|---|---|
| P B Sulekha and ... zation of..Nov.2001PDF.PDF | (4.151Mb) |
| Abstract: | Research in the fields of ceramic pigments is oriented towards the enlargement of the chromatic set of colors together with a replacement for more expensive and less stable organic pigments. Novel non-toxic inorganic pigments have been required to answer environmental laws to remove elements like lead, chromium, cobalt entering in the composition of usual pigments widely used in paints and plastics. Yellow is particularly an important color in the pigment industry and consumption of yellow exceeds that of any other colored pigments. Apart from this, high infrared reflective pigments are now in great demand for usage in coatings, cement pavements, automotives and camouflage applications. They not only impart color to an object, but also reflect the invisible heat from the object to minimize heat build–up, when exposed to solar radiation. With this in view, the present work aims at developing new functional yellow pigments for these applications. A series of IR reflecting yellow pigments have been synthesized and analyzed for their crystalline structure, morphological, composition and optical characteristics, coloring and energy saving applications |
| URI: | http://dyuthi.cusat.ac.in/purl/5099 |
| Files | Size |
|---|---|
| Dyuthi-T 2165 .pdf | (12.19Mb) |
| Abstract: | Novel thermo-reversible zinc sulphonated ionomers based on styrene butadiene rubber (SBR), and high styrene rubber (HSH) were synthesized by sulphonation followed by neutralization with zinc. The sulphonate content of the ionomer was estimated by using x-ray fluorescence spectroscopy. Presence of sulphonate groups has been confirmed by FTIR and FTNMR spectra. The TGA results show improvement in the thermo~oxidative stability of the modified rubber. Both DSC and DMTA studies show that the incorporation of the ionic groups affect the glass rubber transition of the base polymer. lntroduction ol ionic functionality in to the base material improved the physical properties. Retention of the improved physical properties of the novel ionomers even after three repeated cycles of mixing and molding may be considered as the evidence for the reprocessability of the ionomer. Effect of particulate fillers (HAF black, silica and zinc stearate) on the properties of the zinc sulphonated styrene butadiene rubber ionomer has been evaluated. Incorporation of tillers results in improvement in mechanical properties. Zinc stearate plays the dual role of reinforcement and plasticization. The evaluation of dielectric properties of zinc sulphonated styrene butadiene rubber iorpmers at microwave frequencies reveal that the materials show conductivity at semiconductor level. The real and imaginary parts of the complex permittivity increases with increase in ionic functionality. Use of the 38.5 ZnS-SBR ionomer as a compatibiliser for obtaining the technologically compatible blends from the immiscible SBR/NBR system has been discussed. |
| Description: | Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/3060 |
| Files | Size |
|---|---|
| Dyuthi-T1034.pdf | (3.420Mb) |
| Abstract: | Poly(amidoamine) dendrimers were synthesized on cross-linked aminomethyl polystyrene. Palladium complexes of supported dendrimers prepared by ligand exchange method were reduced to dendrimernanoparticle conjugates supported on polystyrene resin. The supported nanoparticles were used as heterogeneous catalysts for the Suzuki coupling between aryl boronic acids and aryl halides. Various factors affecting the catalysts performance were studied. Higher generation dendrimers gave well-defined nanoparticles without agglomeration and these particles showed good catalytic performance |
| Description: | Soft Materials, 8(2):114–129, (2010) |
| URI: | http://dyuthi.cusat.ac.in/purl/4016 |
| Files | Size |
|---|---|
| Synthesis and C ... anoparticle Conjugates.pdf | (1.104Mb) |
| Abstract: | Some new transition metal complexes of the Schiff base quinoxaline-2-car boxalidene-2-aminophenol (HQAP) have been synthesized and characterized by elemental analyses, conductance and magnetic measurements and IR and UV-Visible spectral studies. The complexes have the following empirical formulae: [Mn(QAP121, [Fe(QAPl2C1I, [Co(QAPl21, [Ni(QAP121 and [Cu(QAP121. A tetrahedral structure has been assigned for the manganese(=), cobalt(II1, nickel(II1 and copper(II1 complexes. For the iron(IIIl complex an octahedral dimeric structure has been suggested |
| URI: | http://dyuthi.cusat.ac.in/purl/1651 |
| Files | Size |
|---|---|
| maya, yusuff.pdf | (374.4Kb) |
| Abstract: | In this work polymers belonging to polyaniline and polyaniline doped with camphor sulphonic acid are synthesised. Cobalt phthalocyanine is an interesting candidate belonging to the tetramers. Studies on the composites containing cobalt phthalocyanine tetramer and polyaniline doped with camphor sulphonic acid for various concentration are also undertaken in order to understand the mechanism. RF plasma polymerised aniline and furfural are prepared. The structural and electrical properties are evaluated. The bombardment of swift heavy ions of these films are carried out and the effect of irradiation on their properties is also investigated. |
| Description: | Department of Physics, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/2183 |
| Files | Size |
|---|---|
| Dyuthi-T0533.pdf | (5.266Mb) |
| Abstract: | Coordination chemistry of schiff bases is of considerable interest due to their various magnetic, catalytic and biological applications. Here it describes the spectral characterization of schiff bases and its Mn (II), Cu (II) and Ni (II) complexes. Then synthesis and spectral characterization of Zn (II), Cd (II) and Co (II) complexes of schiff base derived from 3-Formylsalicilic Acid and 1,3-diaminopropane. Then it discusses the synthesis and spectral studies of Copper (II) complexes of 2-Hydroxyacetophenone N-phenyl semicarbazone. Finally it discusses the synthesis and spectral characterization of Co (III) complexes of salicylaldehyde N-phenyl semicarbazone. The preparation and characterization of Cobalt (III) complexes of salicylaldehyde, N-phenylthiosemicarbazone containing hetrocyclic bases phenalthroline and bipyridine. Thiocyanate, azide and perchlorate ions act as coligands. Elemental analysis suggests +3 state for Cobalt. HNMR, IR and UV-visible spectra characterize the complexes. |
| URI: | http://dyuthi.cusat.ac.in/purl/17 |
| Files | Size |
|---|---|
| Dyuthi-T0270.pdf | (1.630Mb) |
| Abstract: | Tellurite glasses are photonic materials of special interest to the branch of optoelectronic and communication, due to its important optical properties such as high refractive index, broad IR transmittance, low phonon energy etc. Tellurite glasses are solutions to the search of potential candidates for nonlinear optical devices. Low phonon energy makes it an efficient host for dopant ions like rare earths, allowing a better environment for radiative transitions. The dopant ions maintain majority of their individual properties in the glass matrix. Tellurites are less toxic than chalcogenides, more chemically and thermally stable which makes them a highly suitable fiber material for nonlinear applications in the midinfrared and they are of increased research interest in applications like laser, amplifier, sensor etc. Low melting point and glass transition temperature helps tellurite glass preparation easier than other glass families. In order to probe into the versatility of tellurite glasses in optoelectronic industry; we have synthesized and undertaken various optical studies on tellurite glasses. We have proved that the highly nonlinear tellurite glasses are suitable candidates in optical limiting, with comparatively lower optical limiting threshold. Tuning the optical properties of glasses is an important factor in the optoelectronic research. We have found that thermal poling is an efficient mechanism in tuning the optical properties of these materials. Another important nonlinear phenomenon found in zinc tellurite glasses is their ability to switch from reverse saturable absorption to saturable absorption in the presence of lanthanide ions. The proposed thesis to be submitted will have seven chapters |
| Description: | International School of Photonics, Cochin University of Science and Technology |
| URI: | http://dyuthi.cusat.ac.in/purl/3558 |
| Files | Size |
|---|---|
| Dyuthi-T1540.pdf | (5.846Mb) |
| Abstract: | Tellurite glasses are photonic materials of special interest to the branch of optoelectronic and communication, due to its important optical properties such as high refractive index, broad IR transmittance, low phonon energy etc. Tellurite glasses are solutions to the search of potential candidates for nonlinear optical devices. Low phonon energy makes it an efficient host for dopant ions like rare earths, allowing a better environment for radiative transitions. The dopant ions maintain majority of their individual properties in the glass matrix. Tellurites are less toxic than chalcogenides, more chemically and thermally stable which makes them a highly suitable fiber material for nonlinear applications in the midinfrared and they are of increased research interest in applications like laser, amplifier, sensor etc. Low melting point and glass transition temperature helps tellurite glass preparation easier than other glass families.In order to probe into the versatility of tellurite glasses in optoelectronic industry; we have synthesized and undertaken various optical studies on tellurite glasses. We have proved that the highly nonlinear tellurite glasses are suitable candidates in optical limiting, with comparatively lower optical limiting threshold. Tuning the optical properties of glasses is an important factor in the optoelectronic research. We have found that thermal poling is an efficient mechanism in tuning the optical properties of these materials. Another important nonlinear phenomenon found in zinc tellurite glasses is their ability to switch from reverse saturable absorption to saturable absorption in the presence of lanthanide ions. The proposed thesis to be submitted will have seven chapters. |
| URI: | http://dyuthi.cusat.ac.in/purl/5119 |
| Files | Size |
|---|---|
| Dyuthi-T 2184.pdf | (5.843Mb) |
| Abstract: | Acicular FeC~O4-2H20 was precipitated from glycerol and starch media. Thermal decomposition of this oxalate in dry and moist nitrogen yielded primarily FeO and Fe 3Oa respectively. Characterization was attempted through DTA, TG, x-ray diffraction, TEM and magnetization studies. It was found that the oxalate can be completely decomposed to FeaO~ in moist nitrogen (PH~o ,"-" 35 torr) at 775 K and then oxidised by dry air to acicular "/-Fe~Oa at 575 K. The resulting material has saturation magnetization (,-,., 70 emu/g), coercive field (N300 Oe) and squareness ratio ( ,~, 0-60-0-65), which values art comparable with those of the commercial samples |
| Description: | Bull. Mater. Sci,, Vol, 3, Number 3, November 1981, pp. 275-280. |
| URI: | http://dyuthi.cusat.ac.in/purl/4419 |
| Files | Size |
|---|---|
| Synthesis and c ... magnetic tape material.pdf | (317.5Kb) |